Chifukwa cha kukula, kampani yathu ili ndi makina osankhira kukula kwa arc a Keyence, omwe amachepetsa chiopsezo chobwera chifukwa cha gulu loyipa la msonkhano wowongolera gawo lamakasitomala.
Ziribe kanthu kuti ❖ kuyanika kwamtundu wanji, tonsefe titha kutsimikizira chithandizo chapadera cha arc pamwamba pa gawo la colloid kuyanjana kwa maginito kuti athetse njira zomwe zimagwiritsidwa ntchito pogwiritsira ntchito ndodo, kukangana kwa guluu wophatikizidwa sikukwanira ndi zina zotero.
Pakuti mawu yobereka, tili ndi zosiyanasiyana akusowekapo mu makulidwe osiyanasiyana ndi sukulu, kupanga prototype maginito nthawi iliyonse.Timayitanitsa ufa wambiri pasadakhale kuti ukadaulo wosinthika wa alloy wapawiri ukwaniritse zofunikira zoperekera makasitomala pambuyo polandila makasitomala.
Kampani yathu ili ndi gulu laukadaulo ndi malonda omwe amatha kupereka upangiri waukadaulo, chiwembu chophatikizira maginito, ndi kuchuluka kwamilandu yogwiritsira ntchito nthawi iliyonse kuwonetsetsa kuti mulibe nkhawa zowonjezera pogwiritsira ntchito makasitomala.
Timatsatira mosamalitsa miyezo yoyendetsera kayendetsedwe ka kayendetsedwe kake, kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe ka kayendetsedwe kamwemwe kapa kapabubumwemwemwemwedwedwe kuyi lughadwe yi kapaso kuyiyitsidwe kachitsulo sikayiyitsidwe kachulukichuluke ndichuluke molingana ndi kachitidwe ka IATF16949 kuwonetsetse kuti makasitomala amaperekedwa ndi kuwunika.
NdFeB Production Process
Coating Introduction
Pamwamba | Kupaka | Makulidwe μm | Mtundu | Maola a SST | Maola a PCT | |
Nickel | Ni | 10-20 | Siliva Wowala | > 24 ~ 72 | > 24 ~ 72 | |
Ni+Cu+Ni | ||||||
Black Nickel | Ni+Cu+Ni | 10-20 | Bright Black | > 48-96 | > 48 | |
Cr3 + Zinc | Zn C-Zn | 5; 8 | Brighe Blue Mtundu Wowala | > 16-48 > 36-72 | --- | |
Sn | Ni+Cu+Ni+Sn | 10-25 | Siliva | > 36-72 | > 48 | |
Au | Ni+Cu+Ni+Au | 10-15 | Golide | > 12 | > 48 | |
Ag | Ni+Cu+Ni+Ag | 10; 15 | Siliva | > 12 | > 48 | |
Epoxy | Epoxy | 10-20 | Black/Grey | > 48 | --- | |
Ndi+Cu+Epoxy | 15-30 | > 72-108 | --- | |||
Zn+Epoxy | 15-25 | > 72-108 | --- | |||
Passivation | --- | 1; 3 | Imvi Yakuda | Chitetezo Chakanthawi | --- | |
Phosphate | --- | 1; 3 | Imvi Yakuda | Chitetezo Chakanthawi) | --- |
Makhalidwe Athupi
Kanthu | Parameters | Mtengo Wothandizira | Chigawo |
Magnetic Wothandizira Katundu | Reversible Temperature Coefficient of Br | -0.08--0.12 | %/℃ |
Kusintha kwa Kutentha Kokwanira Kwa Hcj | -0.42-0.70 | %/℃ | |
Kutentha Kwapadera | 0.502 | KJ ·(Kg ·℃)-1 | |
Curie Kutentha | 310-380 | ℃ | |
Mechanical Physical Katundu | Kuchulukana | 7.5-7.80 | g/cm3 |
Vickers Kuuma | 650 | Hv | |
Kukaniza Magetsi | 1.4x10-6 | μq m | |
Compressive Mphamvu | 1050 | MPa | |
Kulimba kwamakokedwe | 80 | Mpa | |
Kupindika Mphamvu | 290 | Mpa | |
Thermal Conductivity | 6 mpaka 8.95 | W/m · K | |
Young's Modulus | 160 | GPA | |
Kukula kwa Thermal(C⊥) | -1.5 | 10-6/℃-1 | |
Kukula kwa Thermal (CII) | 6.5 | 10-6/℃-1 |